Pérdidas magnéticas en materiales amorfos y nanocristalinos

  1. PEREZ DEL REAL, RAFAEL
Supervised by:
  1. Antonio Hernando Grande Director

Defence university: Universidad Complutense de Madrid

Year of defence: 1994

Committee:
  1. Salvador Velayos Hermida Chair
  2. Claudio Aroca Hernández-Ros Secretary
  3. José Rivas Committee member
  4. Marcos Tejedor Gancedo Committee member
  5. Manuel Vázquez Villalabeitia Committee member

Type: Thesis

Teseo: 43123 DIALNET

Abstract

EN ESTE TRABAJO SE HA ESTUDIADO EL COMPORTAMIENTO DE LAS PERDIDAS MAGNETICAS CON RESPECTO A LOS TRATAMIENTOS TERMICOS EFECTUADOS EN MATERIALES DE COMPOSICION FE73.5CUNB3SI16.5B6. SE HA COMPROBADO QUE CUANDO LAS MUESTRAS SON RECOCIDAS A 550 C DURANTE UNA HORA SE PRODUCE LA REDUCCION DE LAS PERDIDAS MAGNETICAS DEBIDO A LA APARICION DE NANOCRISTALES DE FESI, LO QUE CONLLEVA LA REDUCCION DE LA MAGNETOSTRICCION. SIN EMBARGO, CUANDO LA MUESTRA ES RECOCIDA A 650 C DURANTE UNA HORA, SE PRODUCE UN GRAN AUMENTO DE LAS PERDIDAS POR HISTERESIS, APARECIENDO ADEMAS UNA RELAJACION QUE SE PODRIA ASOCIAR A LA APARICION DE NANOCRISTALES DE FEB. POR OTRA PARTE, MUESTRAS DE LA MISMA COMPOSICION HAN SIDO RECUBIERTAS CON SIO2 MEDIANTE PULVERIZACION CATODICA. AL RECOCER LAS MUESTRAS RECUBIERTAS A 550 C UNA HORA SE HA OBSERVADO LA APARICION DE UNA ANISOTROPIA MAGNETICA TRANSVERSAL AL EJE DE LA CINTA Y PRODUCIDA POR LAS "BACK STRESSES" QUE APARECEN DURANTE EL TRATAMIENTO. CON ESTA ANISOTROPIA AUMENTAN LAS PERDIDAS POR HISTERESIS, MIENTRAS QUE SE PRODUCE UNA TENUE RELAJACION (OBSERVADA EN LAS PERDIDAS POR CICLO POR UNIDAD DE VOLUMEN) ASOCIADA A LA APARICION DE LOS NANOCRISTALITOS DE FESI.